Photoresist composition and method of manufacturing a semiconductor device

ABSTRACT

A photoresist composition includes a photoactive compound and a polymer. The polymer has a polymer backbone including one or more groups selected from:The polymer backbone includes at least one group selected from B, C-1, or C-2, wherein ALG is an acid labile group, and X is linking group.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority to U.S. Provisional Patent Application No. 62/982,719, filed Feb. 27, 2020, the entire disclosure of which is incorporated herein by reference.

BACKGROUND

As consumer devices have gotten smaller and smaller in response to consumer demand, the individual components of these devices have necessarily decreased in size as well. Semiconductor devices, which make up a major component of devices such as mobile phones, computer tablets, and the like, have been pressured to become smaller and smaller, with a corresponding pressure on the individual devices (e.g., transistors, resistors, capacitors, etc.) within the semiconductor devices to also be reduced in size.

One enabling technology that is used in the manufacturing processes of semiconductor devices is the use of photolithographic materials. Such materials are applied to a surface of a layer to be patterned and then exposed to an energy that has itself been patterned. Such an exposure modifies the chemical and physical properties of the exposed regions of the photosensitive material. This modification, along with the lack of modification in regions of the photosensitive material that were not exposed, can be exploited to remove one region without removing the other.

However, as the size of individual devices has decreased, process windows for photolithographic processing has become tighter and tighter. As such, advances in the field of photolithographic processing are necessary to maintain the ability to scale down the devices, and further improvements are needed in order to meet the desired design criteria such that the march towards smaller and smaller components may be maintained.

As the semiconductor industry has progressed into nanometer technology process nodes in pursuit of higher device density, higher performance, and lower costs, there have been challenges in reducing semiconductor feature size. Extreme ultraviolet lithography (EUVL) has been developed to form smaller semiconductor device feature size and increase device density on a semiconductor wafer. In order to improve EUVL an increase in wafer exposure throughput is desirable. Wafer exposure throughput can be improved through increased exposure power or increased resist photospeed.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure is best understood from the following detailed description when read with the accompanying figures. It is emphasized that, in accordance with the standard practice in the industry, various features are not drawn to scale and are used for illustration purposes only. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIG. 1 illustrates a process flow of manufacturing a semiconductor device according to embodiments of the disclosure.

FIG. 2 shows a process stage of a sequential operation according to an embodiment of the disclosure.

FIGS. 3A and 3B show a process stage of a sequential operation according to an embodiment of the disclosure.

FIG. 4 shows a process stage of a sequential operation according to an embodiment of the disclosure.

FIG. 5 shows a process stage of a sequential operation according to an embodiment of the disclosure.

FIG. 6 shows a process stage of a sequential operation according to an embodiment of the disclosure.

FIG. 7 shows polymers according to some embodiments of the disclosure.

FIG. 8 shows a process stage of a sequential operation according to an embodiment of the disclosure.

FIGS. 9A and 9B show a process stage of a sequential operation according to an embodiment of the disclosure.

FIG. 10 shows a process stage of a sequential operation according to an embodiment of the disclosure.

FIG. 11 shows a process stage of a sequential operation according to an embodiment of the disclosure.

FIG. 12 shows a process stage of a sequential operation according to an embodiment of the disclosure.

DETAILED DESCRIPTION

It is to be understood that the following disclosure provides many different embodiments, or examples, for implementing different features of the disclosure. Specific embodiments or examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, dimensions of elements are not limited to the disclosed range or values, but may depend upon process conditions and/or desired properties of the device. Moreover, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed interposing the first and second features, such that the first and second features may not be in direct contact. Various features may be arbitrarily drawn in different scales for simplicity and clarity.

Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The device may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly. In addition, the term “made of” may mean either “comprising” or “consisting of.”

FIG. 1 illustrates a process flow 100 of manufacturing a semiconductor device according to embodiments of the disclosure. A photoresist composition is coated on a surface of a layer to be patterned (target layer) or a substrate 10 in operation S110, in some embodiments, to form a photoresist layer 15, as shown in FIG. 2 . Then the photoresist layer 15 undergoes a first baking operation S120 (pre-exposure baking) to evaporate solvents in the photoresist composition in some embodiments. The photoresist layer 15 is baked at a temperature and time sufficient to cure and dry the photoresist layer 15. In some embodiments, the photoresist layer is heated to a temperature of about 40° C. to 120° C. for about 10 seconds to about 10 minutes. Heating at temperatures below the disclosed ranges or for less the than disclosed time duration may result in insufficient solvent removal from the photoresist layer. Heating at temperatures above the disclosed range or for longer than the disclosed time duration may result in deleterious chemical reactions in the photoresist layer. In some embodiments, the photoresist layer 15 has a thickness of less than 75 nm. In some embodiments, the thickness of the photoresist layer 15 ranges from about 10 nm to about 75 nm, in other embodiments, the thickness of the photoresist layer 15 ranges from about 25 nm to about 65 nm. Thicknesses of the photoresist layer less than the disclosed ranges may result in insufficient photoresist coverage of the subsequently formed photoresist pattern. Thicknesses of the photoresist layer greater than the disclosed range may result in unnecessarily thick photoresist layers, higher cost of the photoresist material, and reduced pattern resolution.

After the first baking operation S120, the photoresist layer 15 is selectively exposed to actinic radiation 45/97 (see FIGS. 3A and 3B) in operation S130. In some embodiments, the photoresist layer 15 is selectively exposed to ultraviolet radiation. In some embodiments, the ultraviolet radiation is deep ultraviolet radiation (DUV). In some embodiments, the ultraviolet radiation is extreme ultraviolet (EUV) radiation. In some embodiments, the radiation is an electron beam.

As shown in FIG. 3A, the exposure radiation 45 passes through a photomask 30 before irradiating the photoresist layer 15 in some embodiments. In some embodiments, the photomask has a pattern to be replicated in the photoresist layer 15. The pattern is formed by an opaque pattern 35 on the photomask substrate 40, in some embodiments. The opaque pattern 35 may be formed by a material opaque to ultraviolet radiation, such as chromium, while the photomask substrate 40 is formed of a material that is transparent to ultraviolet radiation, such as fused quartz.

In some embodiments, the selective exposure of the photoresist layer 15 to form exposed regions 50 and unexposed regions 52 is performed using extreme ultraviolet lithography. In an extreme ultraviolet lithography operation a reflective photomask 65 is used to form the patterned exposure light, as shown in FIG. 3B. The reflective photomask 65 includes a low thermal expansion glass substrate 70, on which a reflective multilayer 75 of Si and Mo is formed. A capping layer 80 and absorber layer 85 are formed on the reflective multilayer 75. A rear conductive layer 90 is formed on the back side of the low thermal expansion substrate 70. In extreme ultraviolet lithography, extreme ultraviolet radiation 95 is directed towards the reflective photomask 65 at an incident angle of about 6°. A portion 97 of the extreme ultraviolet radiation is reflected by the Si/Mo multilayer 75 towards the photoresist-coated substrate 10, while the portion of the extreme ultraviolet radiation incident upon the absorber layer 85 is absorbed by the photomask. In some embodiments, additional optics, including mirrors, are between the reflective photomask 65 and the photoresist-coated substrate.

The region of the photoresist layer exposed to radiation 50 undergoes a chemical reaction thereby changing its solubility in a subsequently applied developer relative to the region of the photoresist layer not exposed to radiation 52. In some embodiments, the portion of the photoresist layer exposed to radiation 50 becomes more soluble in a developer. In some embodiments, the portion of the photoresist layer exposed to radiation 50 undergoes a crosslinking reaction.

Next, the photoresist layer 15 undergoes a post-exposure bake (PEB) (or second baking) in operation S140. In some embodiments, the photoresist layer 15 is heated to a temperature of about 50° C. to 160° C. for about 20 seconds to about 120 seconds. The post-exposure baking may be used in order to assist in the generating, dispersing, and reacting of the acid/base/free radical generated from the impingement of the radiation 45/97 upon the photoresist layer 15 during the exposure. Such assistance helps to create or enhance chemical reactions, which generate chemical differences between the exposed region 50 and the unexposed region 52 within the photoresist layer. These chemical differences also cause differences in the solubility between the exposed region 50 and the unexposed region 52. Heating at temperatures below the disclosed ranges or for less the than disclosed time duration may result in insufficient generation, dispersing, and reaction of the acid/base/free radical. Heating at temperatures above the disclosed range or for longer than the disclosed time duration may result in deleterious chemical reactions in the photoresist layer or may unnecessarily increase the cost and processing time of the semiconductor device.

The selectively exposed photoresist layer is subsequently developed by applying a developer to the selectively exposed photoresist layer in operation S150. As shown in FIG. 4 , a developer 57 is supplied from a dispenser 62 to the photoresist layer 15. In some embodiments, the exposed portion of the photoresist layer 50 is removed by the developer 57 forming a pattern of openings 55 in the photoresist layer 15 to expose the substrate 10, as shown in FIG. 5 .

In some embodiments, the pattern of openings 55 in the photoresist layer 15 are extended into the layer to be patterned or substrate 10 to create a pattern of openings 55′ in the substrate 10, thereby transferring the pattern in the photoresist layer 15 into the substrate 10, as shown in FIG. 6 . The pattern is extended into the substrate by etching, using one or more suitable etchants. The unexposed photoresist layer 52 is at least partially removed during the etching operation in some embodiments. In other embodiments, the unexposed photoresist layer 52 is removed after etching the substrate 10 by using a suitable photoresist stripper solvent or by a photoresist ashing operation.

In some embodiments, the substrate includes a semiconductor wafer. In some embodiments, the substrate 10 includes a single crystalline semiconductor layer on at least it surface portion. The substrate 10 may include a single crystalline semiconductor material such as, but not limited to Si, Ge, SiGe, GaAs, InSb, GaP, GaSb, InAlAs, InGaAs, GaSbP, GaAsSb and InP. In some embodiments, the substrate 10 is a silicon layer of an SOI (silicon-on insulator) substrate. In certain embodiments, the substrate 10 is made of crystalline Si.

The substrate 10 may include in its surface region, one or more buffer layers (not shown). The buffer layers can serve to gradually change the lattice constant from that of the substrate to that of subsequently formed source/drain regions. The buffer layers may be formed from epitaxially grown single crystalline semiconductor materials such as, but not limited to Si, Ge, GeSn, SiGe, GaAs, InSb, GaP, GaSb, InAlAs, InGaAs, GaSbP, GaAsSb, GaN, GaP, and InP. In an embodiment, the silicon germanium (SiGe) buffer layer is epitaxially grown on the silicon substrate 10. The germanium concentration of the SiGe buffer layers may increase from 30 atomic % for the bottom-most buffer layer to 70 atomic % for the top-most buffer layer.

In some embodiments, the substrate 10 includes one or more layers of at least one metal, metal alloy, and metal nitride/sulfide/oxide/silicide having the formula MX_(a), where M is a metal and X is N, S, Se, O, Si, and a is from about 0.4 to about 2.5. In some embodiments, the substrate 10 includes titanium, aluminum, cobalt, ruthenium, titanium nitride, tungsten nitride, tantalum nitride, and combinations thereof.

In some embodiments, the substrate 10 includes a dielectric having at least a silicon or metal oxide or nitride of the formula MX_(b), where M is a metal or Si, X is N or O, and b ranges from about 0.4 to about 2.5. In some embodiments, the substrate 10 includes silicon dioxide, silicon nitride, aluminum oxide, hafnium oxide, lanthanum oxide, and combinations thereof.

The photoresist layer 15 is a photosensitive layer that is patterned by exposure to actinic radiation. Typically, the chemical properties of the photoresist regions struck by incident radiation change in a manner that depends on the type of photoresist used. Photoresist layers 15 are either positive tone resists or negative tone resists. A positive tone resist refers to a photoresist material that when exposed to radiation, such as UV light, becomes soluble in a developer, while the region of the photoresist that is non-exposed (or exposed less) is insoluble in the developer. A negative tone resist, on the other hand, refers to a photoresist material that when exposed to radiation becomes insoluble in the developer, while the region of the photoresist that is non-exposed (or exposed less) is soluble in the developer. The region of a negative resist that becomes insoluble upon exposure to radiation may become insoluble due to a cross-linking reaction caused by the exposure to radiation.

Whether a resist is a positive tone or negative tone may depend on the type of developer used to develop the resist. For example, some positive tone photoresists provide a positive pattern, (i.e.—the exposed regions are removed by the developer), when the developer is an aqueous-based developer, such as a tetramethylammonium hydroxide (TMAH) solution. On the other hand, the same photoresist provides a negative pattern (i.e.—the unexposed regions are removed by the developer) when the developer is an organic solvent. Further, in some negative tone photoresists developed with the TMAH solution, the unexposed regions of the photoresist are removed by the TMAH, and the exposed regions of the photoresist, that undergo cross-linking upon exposure to actinic radiation, remain on the substrate after development.

In some embodiments, the photoresist layer includes a high sensitivity photoresist composition. In some embodiments, the high sensitivity photoresist composition is highly sensitive to extreme ultraviolet (EUV) radiation.

In some embodiments, the photoresist composition includes a polymer along with one or more photoactive compounds (PACs). In some embodiments, the polymer includes a hydrocarbon structure (such as an alicyclic hydrocarbon structure) that contains one or more groups that will decompose (e.g., acid labile groups) or otherwise react when mixed with acids, bases, or free radicals generated by the PACs (as further described below). In some embodiments, the hydrocarbon structure includes a repeating unit that forms a skeletal backbone of the polymer. This repeating unit may include acrylic esters, methacrylic esters, crotonic esters, vinyl esters, maleic diesters, fumaric diesters, itaconic diesters, (meth)acrylonitrile, (meth)acrylamides, styrenes, vinyl ethers, combinations of these, or the like.

Specific structures that are utilized for the repeating unit of the hydrocarbon structure in some embodiments, include one or more of methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl acrylate, n-butyl acrylate, isobutyl acrylate, tert-butyl acrylate, n-hexyl acrylate, 2-ethylhexyl acrylate, acetoxyethyl acrylate, phenyl acrylate, 2-hydroxyethyl acrylate, 2-methoxyethyl acrylate, 2-ethoxyethyl acrylate, 2-(2-methoxyethoxy)ethyl acrylate, cyclohexyl acrylate, benzyl acrylate, 2-alkyl-2-adamantyl (meth)acrylate or dialkyl(1-adamantyl)methyl (meth)acrylate, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, isobutyl methacrylate, tert-butyl methacrylate, n-hexyl methacrylate, 2-ethylhexyl methacrylate, acetoxyethyl methacrylate, phenyl methacrylate, 2-hydroxyethyl methacrylate, 2-methoxyethyl methacrylate, 2-ethoxyethyl methacrylate, 2-(2-methoxyethoxy)ethyl methacrylate, cyclohexyl methacrylate, benzyl methacrylate, 3-chloro-2-hydroxypropyl methacrylate, 3-acetoxy-2-hydroxypropyl methacrylate, 3-chloroacetoxy-2-hydroxypropyl methacrylate, butyl crotonate, hexyl crotonate, or the like. Examples of the vinyl esters include vinyl acetate, vinyl propionate, vinyl butylate, vinyl methoxyacetate, vinyl benzoate, dimethyl maleate, diethyl maleate, dibutyl maleate, dimethyl fumarate, diethyl fumarate, dibutyl fumarate, dimethyl itaconate, diethyl itaconate, dibutyl itaconate, acrylamide, methyl acrylamide, ethyl acrylamide, propyl acrylamide, n-butyl acrylamide, tert-butyl acrylamide, cyclohexyl acrylamide, 2-methoxyethyl acrylamide, dimethyl acrylamide, diethyl acrylamide, phenyl acrylamide, benzyl acrylamide, methacrylamide, methyl methacrylamide, ethyl methacrylamide, propyl methacrylamide, n-butyl methacrylamide, tert-butyl methacrylamide, cyclohexyl methacrylamide, 2-methoxyethyl methacrylamide, dimethyl methacrylamide, diethyl methacrylamide, phenyl methacrylamide, benzyl methacrylamide, methyl vinyl ether, butyl vinyl ether, hexyl vinyl ether, methoxyethyl vinyl ether, dimethylaminoethyl vinyl ether, or the like. Examples of styrenes include styrene, methyl styrene, dimethyl styrene, trimethyl styrene, ethyl styrene, isopropyl styrene, butyl styrene, methoxy styrene, butoxy styrene, acetoxy styrene, hydroxy styrene, chloro styrene, dichloro styrene, bromo styrene, vinyl methyl benzoate, α-methyl styrene, maleimide, vinylpyridine, vinylpyrrolidone, vinylcarbazole, combinations of these, or the like.

In some embodiments, the repeating unit of the hydrocarbon structure also has either a monocyclic or a polycyclic hydrocarbon structure substituted into it, or the monocyclic or polycyclic hydrocarbon structure is the repeating unit, in order to form an alicyclic hydrocarbon structure. Specific examples of monocyclic structures in some embodiments include bicycloalkane, tricycloalkane, tetracycloalkane, cyclopentane, cyclohexane, or the like. Specific examples of polycyclic structures in some embodiments include adamantane, norbornane, isobornane, tricyclodecane, tetracyclododecane, or the like.

In some embodiments, the polymer has a polymer backbone including one or more of the groups consisting of A, B, C, C-1, C-2, and D, as shown in FIG. 7 , wherein at least one of the polymer backbone groups is a B, C-1, or C-2 group. ALG in FIG. 7 is an acid labile group and X is a linking group. In some embodiments, the acid labile group is one or more of:

In some embodiments, the linking group is a substituted or unsubstituted C6-C30 aryl group, C1-C30 alkyl group, C3-C30 cycloalkyl group, C1-C30 hydroxylalkyl group, C2-C30 alkoxy group, C3-C30 alkoxyl alkyl group, C2-C30 acetyl group, C3-C30 acetylalkyl group, C1-C30 carboxyl group, C2-C30 alkyl carboxyl group, C4-C30 cycloalkyl carboxyl group, saturated or unsaturated C3-C30 hydrocarbon ring, saturated or unsaturated C1-C30 heterocyclic group, or C1-C30 chain, ring, or 3-D structure. Each of the above groups may be substituted with one or more substituents, including a halogen, such as a fluoro, chloro, bromo, or iodo group; or an amino group. In some embodiments, the C6-C30 aryl group includes benzyl groups; phenyl groups; or fused aryl groups, including naphthalenyl, and anthracenyl groups. In some embodiments, the linking group is an ester group or a long chain hydrocarbon. In some embodiments, the polymer includes 40 wt. % to 70 wt. % of one or more of groups B, C-1, and C-2 based on a total polymer weight. In some embodiments, the pendant groups on the backbone polymer include two or three ALGs. In some embodiments, the ALG includes a hydroxyl group that enables tuning of the dissolution rate of the ALG in the developer solvent.

In some embodiments, the polymer is a polyhydroxystyrene, a polymethyl methacrylate, or a polyhydroxystyrene-t-butyl acrylate including one or more B, C-1, or C-2 groups from FIG. 7 .

The acid labile group is attached to the hydrocarbon structure so that, it will react with the acids/bases/free radicals generated by the PACs during exposure. In some embodiments, the group which will decompose is a carboxylic acid group, a fluorinated alcohol group, a phenolic alcohol group, a sulfonic group, a sulfonamide group, a sulfonylimido group, an (alkylsulfonyl) (alkylcarbonyl)methylene group, an (alkyl sulfonyl)(alkyl-carbonyl)imido group, a bis(alkylcarbonyl)methylene group, a bis(alkylcarbonyl)imido group, a bis(alkylsulfonyl)methylene group, a bis(alkylsulfonyl)imido group, a tris(alkylcarbonyl methylene group, a tris(alkylsulfonyl)methylene group, combinations of these, or the like. Specific groups that are used for the fluorinated alcohol group include fluorinated hydroxyalkyl groups, such as a hexafluoroisopropanol group in some embodiments. Specific groups that are used for the carboxylic acid group include acrylic acid groups, methacrylic acid groups, or the like.

In some embodiments, such as when EUV radiation is used, the photoresist compositions according to the present disclosure are metal-containing resists. The metal-containing resists include metallic cores complexed with one or more ligands in a solvent. In some embodiments, the resist includes metal particles. In some embodiments, the metal particles are nanoparticles. As used herein, nanoparticles are particles having an average particle size between about 1 nm and about 20 nm. In some embodiments, the metallic cores, including from 1 to about 18 metal particles, are complexed with one or more organic ligands in a solvent. In some embodiments, the metallic cores include 3, 6, 9, or more metal nanoparticles complexed with one or more organic ligands in a solvent.

In some embodiments, the metal particle is one or more of titanium (Ti), zinc (Zn), zirconium (Zr), nickel (Ni), cobalt (Co), manganese (Mn), copper (Cu), iron (Fe), strontium (Sr), tungsten (W), vanadium (V), chromium (Cr), tin (Sn), hafnium (Hf), indium (In), cadmium (Cd), molybdenum (Mo), tantalum (Ta), niobium (Nb), aluminum (Al), cesium (Cs), barium (Ba), lanthanum (La), cerium (Ce), silver (Ag), antimony (Sb), combinations thereof, or oxides thereof. In some embodiments, the metal particles include one or more selected from the group consisting of Ce, Ba, La, In, Sn, Ag, Sb, and oxides thereof.

In some embodiments, the metal nanoparticles have an average particle size between about 2 nm and about 5 nm. In some embodiments, the amount of metal nanoparticles in the resist composition ranges from about 0.5 wt. % to about 15 wt. % based on the weight of the nanoparticles and the solvent. In some embodiments, the amount of nanoparticles in the resist composition ranges from about 5 wt. % to about 10 wt. % based on the weight of the nanoparticles and the solvent. In some embodiments, the concentration of the metal particles ranges from 1 wt. % to 7 wt. % based on the weight of the solvent and the metal particles. Below about 0.5 wt. % metal nanoparticles, the resist coating is too thin. Above about 15 wt. % metal nanoparticles, the resist coating is too thick and viscous.

In some embodiments, the metallic core is complexed by a thermally stable ligand, wherein the thermally stable ligand includes branched or unbranched, cyclic or noncyclic, saturated organic groups, including C1-C7 alkyl groups or C1-C7 fluoroalkyl groups. The C1-C7 alkyl groups or C1-C7 fluoroalkyl groups include one or more substituents selected from the group consisting of —CF₃, —SH, —OH, ═O, —S—, —P—, —PO₂, —C(═O)SH, —C(═O)OH, —C(═O)O—, —O—, —N—, —C(═O)NH, —SO₂OH, —SO₂SH, —SOH, and —SO₂—. In some embodiments, the ligand includes one or more substituents selected from the group consisting of —CF₃, —OH, —SH, and —C(═O)OH substituents.

In some embodiments, the ligand is a carboxylic acid or sulfonic acid ligand. For example, in some embodiments, the ligand is a methacrylic acid. In some embodiments, the metal particles are nanoparticles, and the metal nanoparticles are complexed with ligands including aliphatic or aromatic groups. The aliphatic or aromatic groups may be unbranched or branched with cyclic or noncyclic saturated pendant groups containing 1-9 carbons, including alkyl groups, alkenyl groups, and phenyl groups. The branched groups may be further substituted with oxygen or halogen. In some embodiments, each metal particle is complexed by 1 to 25 ligand units. In some embodiments, each metal particle is complexed by 3 to 18 ligand units.

In some embodiments, the resist composition includes about 0.1 wt. % to about 20 wt. % of the ligands based on the total weight of the resist composition. In some embodiments, the resist includes about 1 wt. % to about 10 wt. % of the ligands. In some embodiments, the ligand concentration is about 10 wt. % to about 40 wt. % based on the weight of the metal particles and the weight of the ligands. Below about 10 wt. % ligand, the organometallic photoresist does not function well. Above about 40 wt. % ligand, it is difficult to form a consistent photoresist layer. In some embodiments, the ligand(s) is dissolved at about a 5 wt. % to about 10 wt. % weight range in a coating solvent, such as propylene glycol methyl ether acetate (PGMEA) based on the weight of the ligand(s) and the solvent.

In some embodiments, the polymers and the PACs, along with any desired additives or other agents, are added to the solvent for application. Once added, the mixture is then mixed in order to achieve a homogenous composition throughout the photoresist to ensure that there are no defects caused by uneven mixing or nonhomogeneous composition of the photoresist. Once mixed together, the photoresist may either be stored prior to its usage or used immediately.

The solvent can be any suitable solvent. In some embodiments, the solvent is one or more selected from propylene glycol methyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), 1-ethoxy-2-propanol (PGEE), γ-butyrolactone (GBL), cyclohexanone (CHN), ethyl lactate (EL), methanol, ethanol, propanol, n-butanol, acetone, dimethylformamide (DMF), isopropanol (IPA), tetrahydrofuran (THF), methyl isobutyl carbinol (MIBC), n-butyl acetate (nBA), and 2-heptanone (MAK).

In some embodiments, the photoresist composition further includes water at a concentration of 10 ppm to 250 ppm based on the total composition of the water, enhancement additive, and first solvent.

In some embodiments, the polymer also includes other groups attached to the hydrocarbon structure that help to improve a variety of properties of the polymer. For example, inclusion of a lactone group to the hydrocarbon structure assists to reduce the amount of line edge roughness after the photoresist has been developed, thereby helping to reduce the number of defects that occur during development. In some embodiments, the lactone groups include rings having five to seven members, although any suitable lactone structure may alternatively be used for the lactone group.

In some embodiments, the polymer includes groups that can assist in increasing the adhesiveness of the photoresist layer 15 to underlying structures (e.g., substrate 10). Polar groups may be used to help increase the adhesiveness. Suitable polar groups include hydroxyl groups, cyano groups, or the like, although any suitable polar group may, alternatively, be used.

Optionally, the polymer includes one or more alicyclic hydrocarbon structures that do not also contain a group, which will decompose in some embodiments. In some embodiments, the hydrocarbon structure that does not contain a group which will decompose includes structures such as 1-adamantyl(meth)acrylate, tricyclodecanyl (meth)acrylate, cyclohexyl (meth)acrylate, combinations of these, or the like.

Some embodiments of the photoresist include one or more photoactive compounds (PACs). The PACs are photoactive components, such as photoacid generators (PAG), photobase (PBG) generators, photo decomposable bases (PDB), free-radical generators, or the like. The PACs may be positive-acting or negative-acting. In some embodiments in which the PACs are a photoacid generator, the PACs include halogenated triazines, onium salts, diazonium salts, aromatic diazonium salts, phosphonium salts, sulfonium salts, iodonium salts, oxime sulfonate, disulfone, o-nitrobenzylsulfonate, sulfonated esters, halogenated sulfonyloxy dicarboximides, diazodisulfones, α-cyanooxyamine-sulfonates, imidesulfonates, ketodiazosulfones, sulfonyldiazoesters, 1,2-di(arylsulfonyl)hydrazines, nitrobenzyl esters, and the s-triazine derivatives, combinations of these, or the like.

Specific examples of photoacid generators include α-(trifluoromethylsulfonyloxy)-bicyclo[2.2.1]hept-5-ene-2,3-dicarb-o-ximide (MDT), N-hydroxy-naphthalimide (DDSN), benzoin tosylate, t-butylphenyl-α-(p-toluenesulfonyloxy)-acetate and t-butyl-α-(p-toluenesulfonyloxy)-acetate, triarylsulfonium and diaryliodonium hexafluoroantimonates, hexafluoroarsenates, trifluoromethanesulfonates, iodonium perfluorooctanesulfonate, N-camphorsulfonyloxynaphthalimide, N-pentafluorophenylsulfonyloxynaphthalimide, ionic iodonium sulfonates such as diaryl iodonium (alkyl or aryl)sulfonate and bis-(di-t-butylphenyl)iodonium camphanylsulfonate, perfluoroalkanesulfonates such as perfluoropentanesulfonate, perfluorooctanesulfonate, perfluoromethanesulfonate, aryl (e.g., phenyl or benzyl)triflates such as triphenylsulfonium triflate or bis-(t-butylphenyl)iodonium triflate; pyrogallol derivatives (e.g., trimesylate of pyrogallol), trifluoromethanesulfonate esters of hydroxyimides, α,α′-bis-sulfonyl-diazomethanes, sulfonate esters of nitro-substituted benzyl alcohols, naphthoquinone-4-diazides, alkyl disulfones, or the like.

In some embodiments in which the PACs are free-radical generators, the PACs include n-phenylglycine; aromatic ketones, including benzophenone, N,N′-tetramethyl-4,4′-diaminobenzophenone, N,N′-tetraethyl-4,4′-diaminobenzophenone, 4-methoxy-4′-dimethylaminobenzo-phenone, 3,3′-dimethyl-4-methoxybenzophenone, p,p′-bis(dimethylamino)benzo-phenone, p,p′-bis(diethylamino)-benzophenone; anthraquinone, 2-ethylanthraquinone; naphthaquinone; and phenanthraquinone; benzoins including benzoin, benzoinmethylether, benzoinisopropylether, benzoin-n-butylether, benzoin-phenylether, methylbenzoin and ethylbenzoin; benzyl derivatives, including dibenzyl, benzyldiphenyldisulfide, and benzyldimethylketal; acridine derivatives, including 9-phenylacridine, and 1,7-bis(9-acridinyl)heptane; thioxanthones, including 2-chlorothioxanthone, 2-methylthioxanthone, 2,4-diethylthioxanthone, 2,4-dimethylthioxanthone, and 2-isopropylthioxanthone; acetophenones, including 1,1-dichloroacetophenone, p-t-butyldichloro-acetophenone, 2,2-diethoxyacetophenone, 2,2-dimethoxy-2-phenylacetophenone, and 2,2-dichloro-4-phenoxyacetophenone; 2,4,5-triarylimidazole dimers, including 2-(o-chlorophenyl)-4,5-diphenylimidazole dimer, 2-(o-fluorophenyl)-4,5-diphenylimidazole dimer, 2-(o-chlorophenyl)-4,5-di-(m-methoxyphenyl imidazole dimer, 2-(o-methoxyphenyl)-4,5-diphenylimidazole dimer, 2-(p-methoxyphenyl)-4,5-diphenylimidazole dimer, 2,4-di(p-methoxyphenyl)-5-phenylimidazole dimer, 2-(2,4-dimethoxyphenyl)-4,5-diphenylimidazole dimer and 2-(p-methylmercaptophenyl)-4,5-diphenylimidazole dimer; combinations of these, or the like.

In some embodiments, the PAC includes photobase generators (PBG) and photo decomposable bases (PDB). In embodiments in which the PACs are photobase generators (PBG), the PBGs include quaternary ammonium dithiocarbamates, a aminoketones, oxime-urethane containing molecules such as dibenzophenoneoxime hexamethylene diurethan, ammonium tetraorganylborate salts, and N-(2-nitrobenzyloxycarbonyl)cyclic amines, combinations of these, or the like.

In some embodiments in which the PACs are photo decomposable bases (PBD), the PBDs include triphenylsulfonium hydroxide, triphenylsulfonium antimony hexafluoride, and triphenylsulfonium trifyl.

As one of ordinary skill in the art will recognize, the chemical compounds listed herein are merely intended as illustrated examples of the PACs and are not intended to limit the embodiments to only those PACs specifically described. Rather, any suitable PAC may be used, and all such PACs are fully intended to be included within the scope of the present embodiments.

In some embodiments, a cross-linking agent is added to the photoresist. The cross-linking agent reacts with one group from one of the hydrocarbon structures in the polymer and also reacts with a second group from a separate one of the hydrocarbon structures in order to cross-link and bond the two hydrocarbon structures together. This bonding and cross-linking increases the molecular weight of the polymer products of the cross-linking reaction and increases the overall linking density of the photoresist. Such an increase in density and linking density helps to improve the resist pattern.

In some embodiments the cross-linking agent has the following structure:

wherein C is carbon, n ranges from 1 to 15; A and B independently include a hydrogen atom, a hydroxyl group, a halide, an aromatic carbon ring, or a straight or cyclic alkyl, alkoxyl/fluoro, alkyl/fluoroalkoxyl chain having a carbon number of between 1 and 12, and each carbon C contains A and B; a first terminal carbon C at a first end of a carbon C chain includes X and a second terminal carbon C at a second end of the carbon chain includes Y, wherein X and Y independently include an amine group, a thiol group, a hydroxyl group, an isopropyl alcohol group, or an isopropyl amine group, except when n=1 then X and Y are bonded to the same carbon C. Specific examples of materials that may be used as the cross-linking agent include the following:

Alternatively, instead of or in addition to the cross-linking agent being added to the photoresist composition, a coupling reagent is added in some embodiments, in which the coupling reagent is added in addition to the cross-linking agent. The coupling reagent assists the cross-linking reaction by reacting with the groups on the hydrocarbon structure in the polymer before the cross-linking reagent, allowing for a reduction in the reaction energy of the cross-linking reaction and an increase in the rate of reaction. The bonded coupling reagent then reacts with the cross-linking agent, thereby coupling the cross-linking agent to the polymer.

Alternatively, in some embodiments in which the coupling reagent is added to the photoresist without the cross-linking agent, the coupling reagent is used to couple one group from one of the hydrocarbon structures in the polymer to a second group from a separate one of the hydrocarbon structures in order to cross-link and bond the two polymers together. However, in such an embodiment the coupling reagent, unlike the cross-linking agent, does not remain as part of the polymer, and only assists in bonding one hydrocarbon structure directly to another hydrocarbon structure.

In some embodiments, the coupling reagent has the following structure:

where R is a carbon atom, a nitrogen atom, a sulfur atom, or an oxygen atom; M includes a chlorine atom, a bromine atom, an iodine atom, —NO₂; —SO₃—; —H—; —CN; —NCO, —OCN; —CO₂—; —OH; —OR*, —OC(O)CR*; —SR, —SO₂N(R*)₂; —SO₂R*; SOR; —OC(O)R*; —C(O)OR*; —C(O)R*; —Si(OR*)₃; —Si(R*)₃; epoxy groups, or the like; and R* is a substituted or unsubstituted C1-C12 alkyl, C1-C12 aryl, C1-C12 aralkyl, or the like. Specific examples of materials used as the coupling reagent in some embodiments include the following:

The individual components of the photoresist are placed into a solvent in order to aid in the mixing and dispensing of the photoresist. To aid in the mixing and dispensing of the photoresist, the solvent is chosen at least in part based upon the materials chosen for the polymer as well as the PACs. In some embodiments, the solvent is chosen such that the polymer and the PACs can be evenly dissolved into the solvent and dispensed upon the layer to be patterned.

In some embodiments, the photoresist composition includes a quencher. The quencher is added to some embodiments of the photoresist composition to inhibit diffusion of the generated acids/bases/free radicals within the photoresist. The quencher improves the resist pattern configuration as well as the stability of the photoresist over time. In an embodiment, the quencher is an amine, such as a second lower aliphatic amine, a tertiary lower aliphatic amine, or the like. Specific examples of amines include trimethylamine, diethylamine, triethylamine, di-n-propylamine, tri-n-propylamine, tripentylamine, diethanolamine, and triethanolamine, alkanolamine, combinations thereof, or the like.

In some embodiments, an organic acid is used as the quencher. Specific embodiments of organic acids include malonic acid, citric acid, malic acid, succinic acid, benzoic acid, salicylic acid; phosphorous oxo acid and its derivatives, such as phosphoric acid and derivatives thereof such as its esters, phosphoric acid di-n-butyl ester and phosphoric acid diphenyl ester; phosphonic acid and derivatives thereof such as its ester, such as phosphonic acid dimethyl ester, phosphonic acid di-n-butyl ester, phenylphosphonic acid, phosphonic acid diphenyl ester, and phosphonic acid dibenzyl ester; and phosphinic acid and derivatives thereof such as its esters, including phenylphosphinic acid.

Another additive added to some embodiments of the photoresist is a stabilizer, which assists in preventing undesired diffusion of the acids generated during exposure of the photoresist. In some embodiments, the stabilizer includes nitrogenous compounds, including aliphatic primary, secondary, and tertiary amines; cyclic amines, including piperidines, pyrrolidines, morpholines; aromatic heterocycles, including pyridines, pyrimidines, purines; imines, including diazabicycloundecene, guanidines, imides, amides, or the like. Alternatively, ammonium salts are also be used for the stabilizer in some embodiments, including ammonium, primary, secondary, tertiary, and quaternary alkyl- and aryl-ammonium salts of alkoxides, including hydroxide, phenolates, carboxylates, aryl and alkyl sulfonates, sulfonamides, or the like. Other cationic nitrogenous compounds, including pyridinium salts and salts of other heterocyclic nitrogenous compounds with anions, such as alkoxides, including hydroxide, phenolates, carboxylates, aryl and alkyl sulfonates, sulfonamides, or the like, are used in some embodiments.

Another additive in some embodiments of the photoresist is a dissolution inhibitor to help control dissolution of the photoresist during development. In an embodiment bile-salt esters may be utilized as the dissolution inhibitor. Specific examples of dissolution inhibitors in some embodiments include cholic acid, deoxycholic acid, lithocholic acid, t-butyl deoxycholate, t-butyl lithocholate, and t-butyl-3-acetyl lithocholate.

Another additive in some embodiments of the photoresist is a plasticizer. Plasticizers may be used to reduce delamination and cracking between the photoresist and underlying layers (e.g., the layer to be patterned). Plasticizers include monomeric, oligomeric, and polymeric plasticizers, such as oligo- and polyethyleneglycol ethers, cycloaliphatic esters, and non-acid reactive steroidaly-derived materials. Specific examples of materials used for the plasticizer in some embodiments include dioctyl phthalate, didodecyl phthalate, triethylene glycol dicaprylate, dimethyl glycol phthalate, tricresyl phosphate, dioctyl adipate, dibutyl sebacate, triacetyl glycerine, or the like.

A coloring agent is another additive included in some embodiments of the photoresist. The coloring agent observers examine the photoresist and find any defects that may need to be remedied prior to further processing. In some embodiments, the coloring agent is a triarylmethane dye or a fine particle organic pigment. Specific examples of materials in some embodiments include crystal violet, methyl violet, ethyl violet, oil blue #603, Victoria Pure Blue BOH, malachite green, diamond green, phthalocyanine pigments, azo pigments, carbon black, titanium oxide, brilliant green dye (C. I. 42020), Victoria Pure Blue FGA (Linebrow), Victoria BO (Linebrow) (C. I. 42595), Victoria Blue BO (C. I. 44045), rhodamine 6G (C. I. 45160), benzophenone compounds, such as 2,4-dihydroxybenzophenone and 2,2′,4,4′-tetrahydroxybenzophenone; salicylic acid compounds, such as phenyl salicylate and 4-t-butylphenyl salicylate; phenylacrylate compounds, such as ethyl-2-cyano-3,3-diphenylacrylate, and 2′-ethylhexyl-2-cyano-3,3-diphenylacrylate; benzotriazole compounds, such as 2-(2-hydroxy-5-methylphenyl)-2H-benzotriazole, and 2-(3-t-butyl-2-hydroxy-5-methylphenyl)-5-chloro-2H-benzotriazole; coumarin compounds, such as 4-methyl-7-diethylamino-1-benzopyran-2-one; thioxanthone compounds, such as diethylthioxanthone; stilbene compounds, naphthalic acid compounds, azo dyes, phthalocyanine blue, phthalocyanine green, iodine green, Victoria blue, naphthalene black, Photopia methyl violet, bromphenol blue and bromcresol green; laser dyes, such as Rhodamine G6, Coumarin 500, DCM (4-(dicyanomethylene)-2-methyl-6-(4-dimethylaminostyryl)-4H pyran)), Kiton Red 620, Pyrromethene 580, or the like. Additionally, one or more coloring agents may be used in combination to provide the desired coloring.

Adhesion additives are added to some embodiments of the photoresist to promote adhesion between the photoresist and an underlying layer upon which the photoresist has been applied (e.g., the layer to be patterned). In some embodiments, the adhesion additives include a silane compound with at least one reactive substituent such as a carboxyl group, a methacryloyl group, an isocyanate group and/or an epoxy group. Specific examples of the adhesion components include trimethoxysilyl benzoic acid, γ-methacryloxypropyl trimethoxy silane, vinyltriacetoxysilane, vinyltrimethoxysilane, γ-isocyanatepropyl triethoxy silane, γ-glycidoxypropyl trimethoxy silane, β-(3,4-epoxycyclohexyl)ethyl trimethoxy silane, benzimidazoles and polybenzimidazoles, a lower hydroxyalkyl substituted pyridine derivative, a nitrogen heterocyclic compound, urea, thiourea, 8-oxyquinoline, 4-hydroxypteridine and derivatives, 1,10-phenanthroline and derivatives, 2,2′-bipyridine and derivatives, benzotriazoles, organophosphorus compounds, phenylenediamine compounds, 2-amino-1-phenylethanol, N-phenylethanolamine, N-ethyldiethanolamine, N-ethylethanolamine and derivatives, benzothiazole, and a benzothiazoleamine salt having a cyclohexyl ring and a morpholine ring, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-mercaptopropyltrimethoxysilane, 3-mercaptopropyltriethoxysilane, 3-methacryloyloxypropyltrimethoxysilane, vinyl trimethoxysilane, combinations thereof, or the like.

Surface leveling agents are added to some embodiments of the photoresist to assist a top surface of the photoresist to be level, so that impinging light will not be adversely modified by an unlevel surface. In some embodiments, surface leveling agents include fluoroaliphatic esters, hydroxyl terminated fluorinated polyethers, fluorinated ethylene glycol polymers, silicones, acrylic polymer leveling agents, combinations thereof, or the like.

In some embodiments, the polymer and the PACs, along with any desired additives or other agents, are added to the solvent for application. Once added, the mixture is then mixed in order to achieve a homogenous composition throughout the photoresist to ensure that there are no defects caused by uneven mixing or nonhomogeneous composition of the photoresist. Once mixed together, the photoresist may either be stored prior to its usage or used immediately.

Once ready, the photoresist is applied onto the layer to be patterned, as shown in FIG. 2 , such as the substrate 10 to form a photoresist layer 15. In some embodiments, the photoresist is applied using a process such as a spin-on coating process, a dip coating method, an air-knife coating method, a curtain coating method, a wire-bar coating method, a gravure coating method, a lamination method, an extrusion coating method, combinations of these, or the like. In some embodiments, the photoresist layer 15 thickness ranges from about 10 nm to about 75 nm.

After the photoresist layer 15 has been applied to the substrate 10 in operation S110, a pre-exposure bake of the photoresist layer is performed in operation S120, in some embodiments, to cure and dry the photoresist prior to radiation exposure (see FIG. 1 ). The curing and drying of the photoresist layer 15 removes the solvent component while leaving behind the polymer, the PACs, and the other chosen additives. In some embodiments, the pre-exposure baking is performed at a temperature suitable to evaporate the solvent, such as between about 40° C. and 120° C., although the precise temperature depends upon the materials chosen for the photoresist. The pre-exposure baking is performed for a time sufficient to cure and dry the photoresist layer, such as between about 10 seconds to about 10 minutes.

FIGS. 3A and 3B illustrate selective exposures of the photoresist layer to form an exposed region 50 and an unexposed region 52. In some embodiments, the exposure to radiation is carried out by placing the photoresist-coated substrate in a photolithography tool. The photolithography tool includes a photomask 30/65, optics, an exposure radiation source to provide the radiation 45/97 for exposure, and a movable stage for supporting and moving the substrate under the exposure radiation.

In some embodiments, the radiation source (not shown) supplies radiation 45/97, such as ultraviolet light, to the photoresist layer 15 in order to induce a reaction of the PACs, which in turn reacts with the polymer to chemically alter those regions of the photoresist layer to which the radiation 45/97 impinges. In some embodiments, the radiation is electromagnetic radiation, such as g-line (wavelength of about 436 nm), i-line (wavelength of about 365 nm), ultraviolet radiation, far ultraviolet radiation, extreme ultraviolet, electron beams, or the like. In some embodiments, the radiation source is selected from the group consisting of a mercury vapor lamp, xenon lamp, carbon arc lamp, a KrF excimer laser light (wavelength of 248 nm), an ArF excimer laser light (wavelength of 193 nm), an F₂ excimer laser light (wavelength of 157 nm), or a CO₂ laser-excited Sn plasma (extreme ultraviolet, wavelength of 13.5 nm).

In some embodiments, optics (not shown) are used in the photolithography tool to expand, reflect, or otherwise control the radiation before or after the radiation 45/97 is patterned by the photomask 30/65. In some embodiments, the optics include one or more lenses, mirrors, filters, and combinations thereof to control the radiation 45/97 along its path.

In an embodiment, the patterned radiation 45/97 is extreme ultraviolet light having a 13.5 nm wavelength, the PAC is a photoacid generator and the group to be decomposed is a carboxylic acid group on the hydrocarbon structure. The patterned radiation 45/97 impinges upon the photoacid generator, and the photoacid generator absorbs the impinging patterned radiation 45/97. This absorption initiates the photoacid generator to generate a proton (e.g., a H⁺ ion) within the photoresist layer 15. When the proton impacts the carboxylic acid group on the hydrocarbon structure, the proton reacts with the carboxylic acid group, chemically altering the carboxylic acid group and altering the properties of the polymer in general.

In some embodiments, the exposure of the photoresist layer 15 uses an immersion lithography technique. In such a technique, an immersion medium (not shown) is placed between the final optics and the photoresist layer, and the exposure radiation 45 passes through the immersion medium.

After the photoresist layer 15 has been exposed to the exposure radiation 45, a post-exposure baking is performed in some embodiments to assist in the generating, dispersing, and reacting of the acid/base/free radical generated from the impingement of the radiation 45 upon the PACs during the exposure. Such thermal assistance helps to create or enhance chemical reactions, which generate chemical differences between the exposed region 50 and the unexposed region 52 within the photoresist layer 15. These chemical differences also cause differences in the solubility between the exposed region 50 and the unexposed region 52. In some embodiments, the post-exposure baking operation S140 occurs at temperatures ranging from about 50° C. to about 160° C. for a period of between about 20 seconds and about 120 seconds. In some embodiments, the post-exposure baking operation is performed at a temperature ranging from about 80° C. to about 100° C.

In some embodiments, the photoresist developer 57 includes a solvent, and an acid or a base. In some embodiments, the concentration of the solvent is from about 60 wt. % to about 99 wt. % based on the total weight of the photoresist developer. The acid or base concentration is from about 0.001 wt. % to about 20 wt. % based on the total weight of the photoresist developer. In certain embodiments, the acid or base concentration in the developer is from about 0.01 wt. % to about 15 wt. % based on the total weight of the photoresist developer.

In some embodiments, the developer 57 is applied to the photoresist layer 15 using a spin-on process. In the spin-on process, the developer 57 is applied to the photoresist layer 15 from above the photoresist layer 15 while the photoresist-coated substrate is rotated, as shown in FIG. 4 . In some embodiments, the developer 57 is supplied at a rate of between about 5 ml/min and about 800 ml/min, while the photoresist coated substrate 10 is rotated at a speed of between about 100 rpm and about 2000 rpm. In some embodiments, the developer is at a temperature of between about 10° C. and about 80° C. The development operation continues for between about 30 seconds to about 10 minutes in some embodiments.

While the spin-on operation is one suitable method for developing the photoresist layer 15 after exposure, it is intended to be illustrative and is not intended to limit the embodiment. Rather, any suitable development operations, including dip processes, puddle processes, and spray-on methods, may alternatively be used. All such development operations are included within the scope of the embodiments.

In some embodiments, the photoresist is a positive tone resist, and during the development process, the developer 57 dissolves the radiation-exposed regions 50 of the positive resist, exposing the surface of the substrate 10, as shown in FIG. 5 , and leaving behind well-defined unexposed photoresist regions 52.

After the developing operation S150, remaining developer is removed from the patterned photoresist covered substrate. The remaining developer is removed using a spin-dry process in some embodiments, although any suitable removal technique may be used. After the photoresist layer 15 is developed, and the remaining developer is removed, additional processing is performed while the patterned photoresist layer 52 is in place. For example, an etching operation, using dry or wet etching, is performed in some embodiments, to transfer the pattern of the photoresist layer 52 to the underlying substrate 10, forming recesses 55″ as shown in FIG. 6 . The substrate 10 has a different etch resistance than the photoresist layer 15. In some embodiments, the etchant is more selective to the substrate 10 than the photoresist layer 15.

In some embodiments, the substrate 10 and the photoresist layer 15 contain at least one etching resistance molecule. In some embodiments, the etching resistant molecule includes a molecule having a low Onishi number structure, a double bond, a triple bond, silicon, silicon nitride, titanium, titanium nitride, aluminum, aluminum oxide, silicon oxynitride, combinations thereof, or the like.

In some embodiments, a target layer 60 is disposed over the substrate 10 prior to forming the photoresist layer, as shown in FIG. 8 . In some embodiments, the target layer 60 is a metallization layer or a dielectric layer, such as a passivation layer, disposed over a metallization layer. In embodiments where the target layer 60 is a metallization layer, the target layer 60 is formed of a conductive material using metallization processes, and metal deposition techniques, including chemical vapor deposition, atomic layer deposition, and physical vapor deposition (sputtering). Likewise, if the target layer 60 is a dielectric layer, the target layer 60 is formed by dielectric layer formation techniques, including thermal oxidation, chemical vapor deposition, atomic layer deposition, and physical vapor deposition.

The photoresist layer 15 is subsequently selectively exposed to actinic radiation 45/97 to form exposed regions 50 and unexposed regions 52 in the photoresist layer, as shown in FIGS. 9A and 9B, and described herein in relation to FIGS. 3A and 3B.

As shown in FIG. 10 , the exposed photoresist regions 50 are developed by dispensing developer 57 from a dispenser 62 to form a pattern of photoresist openings 55, as shown in FIG. 11. The development operation is similar to that explained with reference to FIGS. 4 and 5 , herein.

Then as shown in FIG. 12 , the pattern 55 in the photoresist layer 15 is transferred to the target layer 60 using an etching operation and the photoresist layer is removed, as explained with reference to FIG. 6 to form pattern 55″ in the target layer 60.

Other embodiments include other operations before, during, or after the operations described above. In some embodiments, the disclosed methods include forming semiconductor devices, including fin field effect transistor (FinFET) structures. In some embodiments, a plurality of active fins are formed on the semiconductor substrate. Such embodiments, further include etching the substrate through the openings of a patterned hard mask to form trenches in the substrate; filling the trenches with a dielectric material; performing a chemical mechanical polishing (CMP) process to form shallow trench isolation (STI) features; and epitaxy growing or recessing the STI features to form fin-like active regions. In some embodiments, one or more gate electrodes are formed on the substrate. Some embodiments include forming gate spacers, doped source/drain regions, contacts for gate/source/drain features, etc. In other embodiments, a target pattern is formed as metal lines in a multilayer interconnection structure. For example, the metal lines may be formed in an inter-layer dielectric (ILD) layer of the substrate, which has been etched to form a plurality of trenches. The trenches may be filled with a conductive material, such as a metal; and the conductive material may be polished using a process such as chemical mechanical planarization (CMP) to expose the patterned ILD layer, thereby forming the metal lines in the ILD layer. The above are non-limiting examples of devices/structures that can be made and/or improved using the method described herein.

In some embodiments, active components such diodes, field-effect transistors (FETs), metal-oxide semiconductor field effect transistors (MOSFET), complementary metal-oxide semiconductor (CMOS) transistors, bipolar transistors, high voltage transistors, high frequency transistors, FinFETs, other three-dimensional (3D) FETs, other memory cells, and combinations thereof are formed, according to embodiments of the disclosure.

The novel photoresist compositions and photolithographic patterning methods according to the present disclosure provide higher semiconductor device feature resolution and density at higher wafer exposure throughput with reduced defects in a higher efficiency process than conventional exposure techniques. The novel photoresist compositions provide improved solubility of the photoresist components in the photoresist composition.

The novel photoresist composition and patterning methods according to the present disclosure provide reduced critical dimension (CD) due to the high numerical aperture (NA) of the photoresist compositions and methods of the present disclosure. However, at high NA the depth of field (DoF) of the photolithographic exposure decreases in accordance with equations 1) and 2):

$\begin{matrix} {{\left. {{{\left. 1 \right){CD}} = {k_{1}\left( {\lambda/{NA}} \right)}}2} \right){NA}} \approx {1/{\left( {2{NA}} \right).}}} &  \end{matrix}$ To counteract the smaller DoF, the thickness of the photoresist layer using photoresist compositions of the present disclosure is reduced in some embodiments compared to other photoresist compositions. The present disclosure provides a photoresist composition and patterning method that has high NA that can be applied in a thin layer because it has high etching resistance. In some embodiments, the thickness of the photoresist layer is less than 75 nm. In some embodiments, compositions and methods according to the present disclosure provide a critical dimension (CD) below 40 nm and a pattern pitch below 80 nm.

An embodiment of the disclosure is a method of manufacturing a semiconductor device, including forming a photoresist layer comprising a photoresist composition over a substrate. The photoresist layer is selectively exposed to actinic radiation to form a latent pattern. The latent pattern is developed by applying a developer to the selectively exposed photoresist layer to form a pattern. The photoresist composition includes a photoactive compound and a polymer. The polymer has a polymer backbone including one or more groups selected from:

and wherein the polymer backbone includes at least one group selected from B, C-1, or C-2, ALG is an acid labile group, and X is a linking group. In an embodiment, the linking group is an ester group. In an embodiment, the acid labile group is one or more of:

In an embodiment, the polymer includes 40 wt. % to 70 wt. % of one or more of groups B, C-1, and C-2 based on a total polymer weight. In an embodiment, the photoactive compound is a photoacid generator. In an embodiment, the photoresist composition includes a solvent. In an embodiment, the photoresist composition includes metal nanoparticles and one or more organic ligands. In an embodiment, the actinic radiation is extreme ultraviolet radiation. In an embodiment, the method includes heating the photoresist layer after selectively exposing the photoresist layer to actinic radiation to form a latent pattern and before developing the latent pattern.

Another embodiment of the disclosure is a method of manufacturing a semiconductor device, including forming a photoresist layer including a photoresist composition over a substrate. The photoresist layer is patternwise exposed to actinic radiation to form a first portion of the photoresist layer that is exposed to the actinic radiation and a second portion of the photoresist layer that is not exposed to the actinic radiation. The second portion of the photoresist layer is removed to form a pattern in the photoresist layer exposing a portion of the substrate, and the pattern in the photoresist layer is extended into the substrate. The photoresist composition includes a photoactive compound and a polymer. The polymer has a polymer backbone including one or more groups selected from:

and wherein the polymer backbone includes at least one group selected from B, C-1, or C-2, ALG is an acid labile group, and X is a linking group. In an embodiment, the linking group is an ester group. In an embodiment, the acid labile group is one or more of:

In an embodiment, the method includes heating the photoresist layer after the patternwise exposing the photoresist layer to actinic radiation. In an embodiment, the method includes heating the photoresist layer before the patternwise exposing the photoresist layer to actinic radiation.

Another embodiment of the disclosure is a photoresist composition, including a photoactive compound and a polymer. The polymer has a polymer backbone including one or more groups selected from:

and wherein the polymer backbone includes at least one group selected from B, C-1, or C-2, ALG is an acid labile group, and X is a linking group. In an embodiment, the linking group is an ester group. In an embodiment, the acid labile group is one or more of:

In an embodiment, the polymer includes 40 wt. % to 70 wt. % of one or more of groups B, C-1, and C-2 based on a total polymer weight. In an embodiment, the photoactive compound is a photoacid generator. In an embodiment, the photoresist composition includes a solvent. In an embodiment, the photoresist composition includes metal nanoparticles and one or more organic ligands.

Another embodiment of the disclosure is a method of manufacturing a semiconductor device including forming a photoresist layer including a photoresist composition over a target layer disposed over a substrate. The photoresist layer is patterned to form a photoresist layer having a pattern exposing a portion of the target layer, and the pattern in the photoresist layer is extended into the target layer. The photoresist composition includes a photoactive compound and a polymer. The polymer has a polymer backbone including one or more groups selected from

and wherein the polymer backbone includes at least one group selected from B, C-1, or C-2, ALG is an acid labile group, and X is a linking group. In an embodiment, the substrate is a semiconductor wafer. In an embodiment, the method includes heating the photoresist layer at a temperature ranging from 40° C. to 120° C. before the patterning photoresist layer. In an embodiment, the patterning the photoresist layer includes selectively exposing the photoresist layer to extreme ultraviolet radiation; and heating the photoresist layer at a temperature ranging from 50° C. to 160° C. after selectively exposing the photoresist layer to extreme ultraviolet radiation. In an embodiment, the acid labile group is one or more of:

In an embodiment, the linking group is a substituted or unsubstituted C6-C30 aryl group, C1-C30 alkyl group, C3-C30 cycloalkyl group, C1-C30 hydroxylalkyl group, C2-C30 alkoxy group, C3-C30 alkoxyl alkyl group, C2-C30 acetyl group, C3-C30 acetylalkyl group, C1-C30 carboxyl group, C2-C30 alkyl carboxyl group, C4-C30 cycloalkyl carboxyl group, saturated or unsaturated C3-C30 hydrocarbon ring, saturated or unsaturated C1-C30 heterocyclic group, or C1-C30 chain, ring, or 3-D structure. In an embodiment, the linking group is an ester group. In an embodiment, the polymer includes 40 wt. % to 70 wt. % of one or more of groups B, C-1, and C-2 based on a total polymer weight. In an embodiment, the photoactive compound is a photoacid generator. In an embodiment, the photoresist composition includes a solvent. In an embodiment, the photoresist composition includes metal nanoparticles and one or more organic ligands.

The foregoing outlines features of several embodiments or examples so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments or examples introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure. 

What is claimed is:
 1. A method of manufacturing a semiconductor device, comprising: forming a photoresist layer comprising a photoresist composition over a substrate; selectively exposing the photoresist layer to actinic radiation to form a latent pattern; and developing the latent pattern by applying a developer to the selectively exposed photoresist layer to form a pattern, wherein the photoresist composition comprises: a photoactive compound; and a polymer, wherein the polymer has a polymer backbone comprising one or more groups selected from:

and wherein the polymer backbone includes at least one group selected from B, C-1, or C-2, ALG is an acid labile group, and X is a linking group.
 2. The method according to claim 1, wherein the linking group is an ester group.
 3. The method according to claim 1, wherein the acid labile group is one or more of:


4. The method according to claim 1, wherein the polymer includes 40 wt. % to 70 wt. % of one or more of groups B, C-1, and C-2 based on a total polymer weight.
 5. The method according to claim 1, wherein the photoactive compound is a photoacid generator.
 6. The method according to claim 1, wherein the photoresist composition further comprises a solvent.
 7. The method according to claim 1, wherein the photoresist composition further comprises metal nanoparticles and one or more organic ligands.
 8. The method according to claim 1, wherein the actinic radiation is extreme ultraviolet radiation.
 9. The method according to claim 1, further comprising after selectively exposing the photoresist layer to actinic radiation to form a latent pattern and before developing the latent pattern heating the photoresist layer.
 10. A method of manufacturing a semiconductor device, comprising: forming a photoresist layer comprising a photoresist composition over a substrate; patternwise exposing the photoresist layer to actinic radiation to form a first portion of the photoresist layer that is exposed to the actinic radiation and a second portion of the photoresist layer that is not exposed to the actinic radiation; removing the second portion of the photoresist layer to form a pattern in the photoresist layer exposing a portion of the substrate; and extending the pattern in the photoresist layer into the substrate, wherein the photoresist composition comprises: a photoactive compound; and a polymer, wherein the polymer has a polymer backbone comprising one or more groups selected from:

and wherein the polymer backbone includes at least one group selected from B, C-1, or C-2, ALG is an acid labile group, and X is a linking group.
 11. The method according to claim 10, wherein the linking group is an ester group.
 12. The method according to claim 10, wherein the acid labile group is one or more of:


13. The method according to claim 10, further comprising heating the photoresist layer after the patternwise exposing the photoresist layer to actinic radiation.
 14. The method according to claim 10, further comprising heating the photoresist layer before the patternwise exposing the photoresist layer to actinic radiation.
 15. A method of manufacturing a semiconductor device, comprising: forming a photoresist layer comprising a photoresist composition over a target layer disposed over a substrate; patterning the photoresist layer to form a photoresist layer having a pattern exposing a portion of the target layer; and extending the pattern in the photoresist layer into the target layer, wherein the photoresist composition comprises: a photoactive compound; and a polymer, wherein the polymer has a polymer backbone comprising one or more groups selected from

and wherein the polymer backbone includes at least one group selected from B, C-1, or C-2, ALG is an acid labile group, and X is a linking group.
 16. The method according to claim 15, wherein the substrate is a semiconductor wafer.
 17. The method according to claim 15, further comprising heating the photoresist layer at a temperature ranging from 40° C. to 120° C. before the patterning photoresist layer.
 18. The method according to claim 15, wherein the patterning the photoresist layer comprises: selectively exposing the photoresist layer to extreme ultraviolet radiation; and heating the photoresist layer at a temperature ranging from 50° C. to 160° C. after selectively exposing the photoresist layer to extreme ultraviolet radiation.
 19. The method according to claim 15, wherein the acid labile group is one or more of:


20. The method according to claim 15, wherein the linking group is a substituted or unsubstituted C6-C30 aryl group, C1-C30 alkyl group, C3-C30 cycloalkyl group, C1-C30 hydroxylalkyl group, C2-C30 alkoxy group, C3-C30 alkoxyl alkyl group, C2-C30 acetyl group, C3-C30 acetylalkyl group, C1-C30 carboxyl group, C2-C30 alky carboxyl group, C4-C30 cycloalkyl carboxyl group, saturated or unsaturated C3-C30 hydrocarbon ring, saturated or unsaturated C1-C30 heterocyclic group, or C1-C30 chain, ring, or 3-D structure. 